Fiberglass Reinforced Phenolic Moulding
- Ton/Tons
- 1
- Ton/Tons
- 3130USD
- Compression Mould
- commutators, solenoid swithch,binding post,brush carrier, starter motor
Fiberglass Reinforced Phenolic Moulding is used to mold, fiber reinforced thermoset polyester material that is ideally applied in compression moulding and injection moulding. Phenolic mouding compound has excellent heat resistance, electrical properties and mechanical strength and are used in electronics and industrial market for many years. This molding compound is known for its excellent finish and safe use. This Fiber Glass Reinforced Phenolic Moulding is checked on various quality parameters before delivering to the customers.
Technical Specifications
| Unit | Standard | Indetexes |
|
| Appearance | / | ZY/ZY .01-2015 | OK |
| Density | g/cm3 | GB/T 1033. 1 | 1.78 |
| Dsic Flow | Cm | ZY/ZY .01-2015 | 18 |
| Flexural strength | MPA | GB/T 9341 | 203 |
| impact strength(unnotchecd) | Kj/m2 | GB/T 1043.1 | 10 |
| Volume resistivity | .cm | GB/T 1410 | 1.01013 |
| (Tf1.8Mpa) | C | GB/T 1634.2 | 230 |
| Moulding shrinkage | % | JB/T6542 | 0.15 |
| Water absorption | % | GB/T 1034 | 0.1 |
| Flame test UL-Subject 94 | UL94 | GB/5169. 16 | V-0 |
| Electric strength | Kv/mm | GB/T 1408.1 | 12 |
| Molding craft |
|
| compressing, transfer processing |
Compression Processing:
| preheating temp. | preheating time | pressure | up mould temp. | down mould temp. | compression temp. | compression speed | pressure keeping time |
| 90-110oC | 120-240S | 20-30MPA | 170oC | 160oC | 160-190oC | 5-20S | 120-240S |
After Curing:
| 150C | 180oC | 210oC | 230oC |
| 2hours | 6hours | 8hours | 3 hours |